JOURNAL OF THE EUROPEAN CERAMIC SOCIETY
卷 41, 期 1, 页码 1033-1040出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.jeurceramsoc.2020.09.018
关键词
Additive manufacturing; screw extrusion; zirconia; fused deposition modeling
资金
- National Natural Science Foundation of China [51572035]
A fused deposition modeling (FDM) system using screw extrusion for feeding granular feedstocks with high solid loading was developed. By optimizing key parameters and determining a processing window, constant extruded mass flow and wire diameter were achieved, leading to successful preparation of zirconia ceramic parts with complex geometries and controlled dimensional accuracy, demonstrating the potential of the technique.
A fused deposition modeling(FDM)system via screw extrusion suitable for feeding granular feedstocks with high solid loading was developed. Key parameters included aspect ratio of the screw, the compression ratio and pitch etc. In order to get constant extruded mass flow and wire diameter a processing window was determined by optimizing the barrel temperature, the nozzle diameter and the screwing speed. Microstructural characterization coupled with flexural strength measurement revealed that a higher printing temperature was beneficial to the inter layer bonding. The sintered zirconia ceramic samples with 99% of theoretical density of the 3 mol% yttria stabilized tetragonal zirconia polycrystal (3Y-TZP) and flexural strength of 890 +/- 60 MPa was obtained. A set of zirconia ceramic parts with complex geometries and controllable dimensional accuracy was also successfully prepared for demonstrating the potential of the technique.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据