期刊
JOURNAL OF NUCLEAR MATERIALS
卷 547, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.jnucmat.2021.152806
关键词
Accident tolerant fuel cladding; Magnetron sputtering; Cold spraying; Chromium coating; Zirconium alloy; Kinetic parameters
资金
- China Scholarship Council [201906280319]
- HGF program NUSAFE at Karlsruhe Institute of Technology (KIT)
This study investigated the Cr-Zr interaction of two types of Cr coated Zr alloy ATF claddings deposited by cold spraying and magnetron sputtering at temperatures ranging from 1100 to 1300 degrees C. It was found that the interlayer growth rate of cold sprayed samples was slightly higher than that of magnetron sputtered samples, and the temperature-dependent consumption coefficient of the Cr coating was calculated.
The Cr-Zr interaction of two types of Cr coated Zr alloy accident tolerant fuel (ATF) claddings, deposited by cold spraying and magnetron sputtering, was studied in argon in the temperature range from 1100 to 1300 degrees C. A tube furnace with a sample lock system was used for fast exchanging samples at test temperature. Inter-diffusion between the coating and the substrate results in the formation of an intermetallic ZrCr2 layer and a solid solution layer beneath. Some pores were formed on the interlayer by a Kirkendall-type mechanism. The interlayer growth rate of cold sprayed samples was always slightly higher than that of magnetron sputtered samples in the same condition. Moreover, the temperature-dependent consumption coefficient of the Cr coating was calculated and fitted to an Arrhenius function. The dissolution and precipitation behavior of Cr in the Zr substrate and the diffusion behavior of Zr in Cr coating were also studied. (C) 2021 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据