Composition and processing of direct-quench hot rolled steels with ultrahigh strength exceeding GPa

期刊

出版社

SPRINGER
DOI: 10.1007/s42243-020-00518-6

关键词

High-strength steel; Direct-quench hot rolling; Bainite morphology; Precipitation; Mechanical property

资金

  1. National Natural Science Foundation of China [51722101, U1808208]
  2. National Key Research and Development Program [2017YFB0304402, 2017YFB0703001]
  3. Joint Project of Benxi Iron and Steel Group Co. [KJB2016004]

向作者/读者索取更多资源

The researchers designed three direct-quench hot rolled steels, successfully increasing strength and reducing production costs by controlling process parameters. They found that lower bainite is superior to granular bainite in terms of strength and low temperature impact toughness. By adjusting grain boundary precipitation, they improved the strength and ductility/toughness of traditional quenched and tempered steels.
The design of high-strength steel has long been discussed in the field of metal structural materials. To further increase the strength of common high-strength steel and further decrease the cost for production, three direct-quench hot rolled steels were designed and fabricated. The rolling and coiling processes were set based on continuous cooling transformation curves. In addition, the effect of the coiling temperature on the tensile properties was discussed to further guide the optimization of the process. It was found that compared with granular bainite, lower bainite probably has more advantages for both the strength and low temperature impact toughness of direct-quench hot rolled steels. Through a process of tailoring the morphology of bainite and controlling the grain boundary precipitation, the newly designed direct-quench hot rolled steels showed greatly improved strength and acceptable ductility/toughness compared with traditional quenched and tempered steels.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据