Effect of Ni(P) thickness in Au/Pd/Ni(P) surface finish on the electrical reliability of Sn-3.0Ag-0.5Cu solder joints during current-stressing

期刊

JOURNAL OF ALLOYS AND COMPOUNDS
卷 850, 期 -, 页码 -

出版社

ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2020.156729

关键词

Current stressing; Electromigration; Electroless-nickel electroless-palladium immersion gold; Sn-3.0Ag-0.5Cu; Time to failure

资金

  1. Ministry of Trade, Industry and Energy, Republic of Korea [20003904]
  2. Korea Evaluation Institute of Industrial Technology (KEIT) [20003904] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)

向作者/读者索取更多资源

The study investigated the effects of Ni(P) layer thickness on the microstructural behavior and electrical reliability of ENEPIG surface-finished printed circuit boards with SAC305 solder joints. The results showed that the Ni(P) layer thickness influenced the growth of IMC layers and electrical performance.
The effects of Ni(P) layer thickness (5 mu m and 0.7 mu m) on the microstructural behavior and electrical reliability of electroless-nickel electroless-palladium immersion gold (ENEPIG) (substrate-side) surface-finished printed circuit boards (PCBs) with Sn-3.0Ag-0.5Cu (SAC305) solder joints under current stressing of 9000 A/cm(2) have been investigated. An organic solderability preservative (OSP) surface finish was applied on the chip-side. (Cu,Ni)(6)Sn-5 and Cu6Sn5 intermetallic compound (IMC) layers were formed on the chip-side (the interface between SAC305 and the OSP surface finish) and substrate-side (the interface between the ENEPIG surface finish and SAC305) solder joints after reflow. The thicknesses of the (Cu,Ni)(6)Sn-5 and Cu6Sn5 IMC layers of the chip- and substrate-side of the normal- and thin-ENEPIG/SAC305/OSP solder joints increased with increasing current stressing time, regardless of the nickel phosphorous (Ni(P)) layer thickness. The total IMC thicknesses of normal-ENEPIG/SAC305/OSP solder joints were relatively thinner than those of thin-ENEPIG/SAC305/OSP solder joints under current stressing for 50-120 h. This is the reason why only a P-rich Ni layer was formed at the interface between SAC305 solder and the Cu pad in the thin-ENEPIG/SAC305 solder joints under current stressing. Otherwise, the P-rich Ni and Ni(P) layers remained at the interface of the normal-ENEPIG/SAC305 solder joint under current stressing. The Ni(P) layer of the ENEPIG surface finish played an important diffusion barrier role by suppressing IMC growth and movement toward the SAC305 solder under current stressing. In the electrical evaluation, the time to failure at the normal-ENEPIG solder joint was relatively longer (approximately 2.2 times) than that of the thin-ENEPIG solder joint. Therefore, the relatively thick Ni(P) layer contained in the ENEPIG/SAC305/OSP solder joint is expected to attain higher electrical reliability under the electromigration test. (C) 2020 Elsevier B.V. All rights reserved.