INTERNATIONAL JOURNAL OF METALCASTING
卷 15, 期 4, 页码 1340-1347出版社
SPRINGER INT PUBL AG
DOI: 10.1007/s40962-020-00564-6
关键词
aluminum matrix composites; pressure infiltration; wear
资金
- Scientific Research Projects Coordination Unit of Karabuk University [KBuBAP-18-YL-149]
Al matrix composites reinforced by a high amount of NiAl (40%) were successfully produced using the pressure infiltration method. Addition of a small amount of Mo into NiAl, along with changing particle sizes, resulted in improved mechanical properties and wear resistance.
In this study, Al matrix composites reinforced by the high amount of NiAl (40%) were produced by the pressure infiltration method. Commercially AA1050 (99.59 %) was used as matrix material and NiAl (at. 1:1) particles were used as reinforcement. Also, a small amount of Mo (wt. 2%) was added into NiAl for a better matrix-particle interface and to increase the mechanical properties. The proportion of particles was kept constant, and their sizes were changed from 45 to 125 mu m. The microstructures were examined by SEM, and formed phases were determined by EDS and XRD analysis. Mechanical properties and wear behavior were determined by compression, hardness, and abrasion tests. As a result of these tests, it was determined that composites were produced successfully. It was determined that compressive strength increased with decreasing particle size. And also, small particle size composites showed higher wear resistance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据