INTERNATIONAL JOURNAL OF FATIGUE
卷 142, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ijfatigue.2020.105964
关键词
Woven fiber; Angle ply; Fatigue; Dynamic modulus; Ratcheting
This study investigated the fatigue behavior of angle plies woven glass fiber reinforced polymer composite laminates through tension-tension fatigue tests under different maximum applied stresses. The results showed that different angles of laminates exhibited global or localized damage during fatigue process.
In this study, fatigue behaviour of angle plies woven glass fiber reinforced polymer (GFRP) composite laminates has been investigated. Tension-tension fatigue tests were carried out under different maximum applied stresses that varied in the range of 50-90% of the respective ultimate strength of the laminates. Damage development in the form of debond zones and their growth was monitored. The results of the study are presented in terms of stress-strain curve, Wohler curve, delamination growth, total dissipated energy, dynamic modulus, and creep strain, respectively. (0 degrees/90 degrees) and +/- 15 degrees laminate witnessed global damage while localized damage occurred in (+/- 30 degrees)8, (+/- 45 degrees)8 laminate.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据