CORROSION SCIENCE
卷 178, 期 -, 页码 -出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.corsci.2020.109058
关键词
Corrosion; Lithium vapour; Aluminium nitride; Mechanism
资金
- National Key Research and Development Program of China [2018YFB0905600]
- Science and Technology Projects of State Grid, State Grid Corporation of China [5100-201999537A-0-0-00]
The study found that in the vapour of lithium, severe cracking along the grain boundary can be observed on the surfaces of aluminium nitride ceramic samples. Possible corrosion failure mechanisms include the dissolution of aluminium nitride in aggregated lithium along the grain boundary. It is expected that high purity aluminium nitride and appropriate doping technology will provide better corrosion resistance under the same conditions.
The corrosion behaviour and possible failure mechanism of aluminium nitride ceramic in the vapour of lithium have been investigated using X-ray diffraction and scanning electron microscope techniques. The results show that severe cracking along the grain boundary can be observed on the surfaces of aluminium nitride samples. Both lithium(yttrium, aluminium) compounds and dissolution of aluminium nitride in the aggregated lithium along the grain boundary are believed to contribute to the corrosion failure. Under the same conditions, high purity aluminium nitride and necessary doping technology are expected to show better corrosion resistance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据