CONSTRUCTION AND BUILDING MATERIALS
卷 264, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2020.120144
关键词
Resin pre-coating (RPC); Subsurface micro-cracks; Repaired structures; Grain size; X-ray Microscopy (XRM)
资金
- National Key R&D Program of China [2018YFC0808702]
- China Scholarship Council [201707000075]
Subsurface micro-defects in rock and concrete-like materials, crucial for the integrity and durability of the epoxy repaired structures, which should be carefully treated during repair. In this study, a Resin Pre-coating (RPC) method was used to seal the subsurface micro-cracks by capillary action. The sandstone (the average grain size G = 0.5 mm) and granite (G = 2 mm) were selected to test the efficiency of RPC method. After the notched three-point-bending (3-p-b) specimens were loaded to fracture, the substrates were bonded together using epoxy adhesive or epoxy adhesive plus RPC. By comparing the peak loads, fracture energy, crack paths, micro-cracking activities before peak load and X-ray Microscopy (XRM) images of subsurface micro-structures of specimens repaired with different methods, the RPC method was proved to be effective for repairing the subsurface micro-cracks and strengthening the repaired structures, meanwhile the efficiency was confirmed to be relevant with the grain size. (C) 2020 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据