Janus membrane; Asymmetric wettability; Emulsion separation; Polydimethylsiloxane; Nanocasting
资金
- National Natural Science Foundation of China [51703099, 51705511]
A simple and low-cost nanocasting/NIPS strategy was reported for the preparation of superhydrophobic and underwater oleophobic Janus membrane, which showed excellent separation performance for both O/W and W/O emulsions.
Janus membrane (JM) with opposite wettability has great potential in separation of oil-in-water (O/W) and water-in-oil (W/O) emulsions. In this work, we have reported a simple, low cost nanocasting/NIPS strategy for preparation of the superhydrophobic and underwater oleophobic surface of JM for the first time. Poly (vinylidene fluoride) (PVDF) and polyethylenimine (PEI) blend membranes were fabricated on PDMS modified nonwoven fabric by non-solvent induced phase separation (NIPS) process. Then the as-prepared membranes were further modified with hydrophilic nano-SiO2 to improve the hydrophilicity of the top surface. Peel off PDMS modified non-woven fabric, parts of PDMS chains were imprinted to the membrane bottom surface with micronano three-dimensional microstructures, resulting in superhydrophobic property. The as-prepared JM exhibits an asymmetric wettability with the water contact angle of 35.3? and 151.8? of the opposite surfaces. By changing the orientation of the membrane, oil or water can be filtered respectively. The as-prepared JM shows excellent separation performance for both O/W emulsion and W/O emulsion, the separation efficiency reached 99.72 % and 99.68 %, respectively, as well as good long-term stability. This work is expected to yield a new way to fabricate the superhydrophobic surface of JM.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据