Self-reinforced porous ceramics; Spearhead columnar mullite; V2O5; Foam-gelcasting
资金
- National Natural Science Foundation of China [51872210, 51672194]
- Program of Hubei Province, China [T201602, 2017CFA004]
The study shows that adding 2% V2O5 can significantly improve the flexural and compressive strength of columnar self-reinforced mullite porous ceramics, while maintaining a low thermal conductivity.
Spearhead columnar mullite was synthesized by in-situ reaction with V2O5 as additive. When the content of V2O5 was 7 wt%, the length of the spearhead columnar mullite was the longest with an aspect ratio of about 3.5. Furthermore, columnar self-reinforced mullite porous ceramics were prepared by a foam-gelcasting method, and the effects of V2O5 content on the rheological and gelling properties of mullite slurries as well as the microstructure, physical property and thermal insulation property of the prepared mullite porous ceramics were studied. The results showed that the flexural strength and compressive strength of the porous ceramics with 63% porosity prepared by using 2 wt% V2O5 additive were respectively as high as 13.9 and 41.3 MPa, and the thermal conductivity was about 1.04 W m(-1) K-1.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据