期刊
CEMENT AND CONCRETE RESEARCH
卷 138, 期 -, 页码 -出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.cemconres.2020.106248
关键词
Cement; Sulfate; C-S-H; Morphology; Gel water; Pores; NMR; SEM; XRD; Calorimetry
The effect of increasing sulfate contents on the hydration of white cement was studied with a multi-technique approach. Quantitative X-Ray Diffraction (XRD) revealed that adding more gypsum in the cement resulted in more ettringite formation. Combining isothermal calorimetry, advanced in-situ H-1 nuclear magnetic resonance (NMR) and early scanning electron microscopy (SEM) observations, it was possible to correlate the depletion of the gypsum with a change in C-S-H morphology, from needle-like to agglomerated C-S-H, together with a change in C-S-H gel pore content. Nevertheless, the content of C-S-H interlayer water remained similar and no change in C-S-H pore sizes were observed when increasing the sulfate content. The data allowed to calculate the volume composition of hydrated cement pastes at 3 days of hydration. The more gypsum was added to the cement, the lower was the bulk C-S-H volume due to lower gel pore content and the higher was the content of capillary porosity.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据