Optimizing Heat Treatment Parameters for the W-Temper Forming of 7xxx Series Aluminum Alloys

期刊

METALS
卷 10, 期 10, 页码 -

出版社

MDPI
DOI: 10.3390/met10101361

关键词

7xxx series aluminum alloys; W-temper forming; room temperature forming; solution heat treatment; retrogression and re-aging; precipitation

向作者/读者索取更多资源

A major challenge in processing 7xxx series aluminum alloys is their limited formability at room temperature. In this paper, for the alloys EN AW-7020 and EN AW-7075, various variants of the W-temper forming process are investigated. For both alloys, a good cold formability and a high strength after aging can be achieved. The effects of solution heat treatment or retrogression temperature and holding time, as well as the influence of plastic deformation after quenching, were studied. For various combinations of process parameters, the formability of the as-quenched materials and the hardening performance during artificial aging were examined. For this, hardness measurements and differential scanning calorimetry (DSC) experiments were performed along the entire process chain, to reveal the development of the hardening precipitates. After solution heat treatment and quenching, the yield stress and hardness of both investigated alloys were drastically reduced in comparison to their initial T6 states, while the ductility was significantly increased. By a subsequent simple artificial aging treatment, the same hardness as in the T6 state could be restored. It was observed that plastic deformation immediately after quenching significantly decreased the artificial aging time to achieve the peak hardness. Besides the conventional solution heat treatment process, an alternative retrogression and re-aging procedure was identified for the alloy EN AW-7020. While the heat treatment temperature can be reduced as compared to the conventional solution heat treatment, the formability and hardenability are equally good. In contrast, no such alternative process could be identified for the alloy EN AW-7075.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据