POLYMER BULLETIN
卷 78, 期 9, 页码 5137-5152出版社
SPRINGER
DOI: 10.1007/s00289-020-03361-7
关键词
Jackfruit gum; Epoxidation; Structural characterization; Polymer solid electrolyte
资金
- Hanoi University of Science and Technology (HUST) [T2018-PC-229]
Epoxidized jackfruit gum (EJG) was prepared and characterized. An attempt was made to prepare a solid polymer electrolyte from EJG, showing improved ion conductivity attributed to the strong interaction between EJG and LiClO4. The epoxy group content of the sample reached 95 mol% after treatment, leading to enhanced ion conductivity.
Epoxidized jackfruit gum (EJG) was prepared and characterized. An attempt to prepare a solid polymer electrolyte from EJG was made. The characterizations of epoxidized jackfruit gum were carried out through FT-IR spectroscopy, NMR spectroscopy, gel permeation chromatography, nitrogen content determination, water uptake determination and ion exchange capacity. The ion conductivity, differential scanning calorimetry, and SEM images of the blends of EJG and LiClO(4)were characterized. The results indicated the epoxy group content of the sample achieved 95 mol% after 3 h of the epoxidation. During the epoxidation, the nitrogen content reduced, whereas the phospholipid content of the samples did not change. The molecular weight of samples reduced during the epoxidation. The ion conductivity of EJG/LiClO4/epoxidized natural rubber was improved, i.e. in order of 10(-4)S/cm which was attributed to the presence of epoxy group in EJG. The liquid crystal may form in EJG/LiClO(4)blends. These phenomena may suggest the strong interaction between epoxy group in EJG and LiClO4.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据