MATERIALS CHEMISTRY AND PHYSICS
卷 253, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.matchemphys.2020.123312
关键词
Polymer electrolytes; CMC-PVA hybrid; Li+; Electrochemical devices
资金
- Ministry of Higher Education (MOHE) of Malaysia through the FRGS grant [FRGS/1/2019/STG07/UMP/02/4: RDU 1901114]
- Universiti Malaysia Pahang [RDU 190398]
- Faculty of Industrial Sciences Technology
In the present work, hybrid polymer electrolytes consisting of a CMC-PVA blend doped with various amounts of LiNO3 was produced using the casting technique. The structural and ionic conductivity of the prepared samples were studied by using Fourier transform infrared (FTIR) spectroscopy, x-ray diffraction (XRD), scanning electron microscopy (SEM) and electrical impedance spectroscopy (EIS) analyses. The optimum ionic conductivity at room temperature was achieved at 3.54 x 10(-3) S cm(-1) with the addition of 20 wt % of LiNO3 which showed the lowest percentage of crystallinity. IR-deconvolution revealed that the ionic conductivity is dependent on the ionic mobility and diffusion coefficient. Linear sweep voltammetry was performed where the highest ionic conducting sample is electrochemically stable up to 1.43 V. The highest conducting sample was fabricated into an electrical double layer capacitor (EDLC) and was characterized by using cyclic voltammetry and galvanostatic charge-discharge (GCD) for their electrochemical stability performance. The GCD profile showed that the fabricated EDLC is stable to operate up to the 5000th cycles with the average specific capacitance of similar to 100 F/g.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据