The microstructures of high strength bainitic steel weldments were characterized, and their hydrogen permeability was investigated by the electrochemical permeation technique. The effective diffusion coefficient in the welded joint increases with heat input, while the hydrogen concentration at the sub-surface decreases with increasing heat input, mainly due to coarsening grain and inclusion sizes. Compared with as-welded specimens, the tempered membranes have lower effective diffusion coefficient and higher density of hydrogen traps due to newly formed carbides acting as hydrogen trapping sites that are derived from the decomposition of martensite-austenite constituents. These were further confirmed by the partial permeation technique. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据