The crystallographic structure of the air-grown oxide on depleted uranium metal

Oxide formation on depleted uranium metal was investigated using a combination of electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM) characterisation. Diffraction analysis of Lthe oxide revealed an FCC crystalline formation of UO2 crystallites whilst TEM data indicated an average grain size of 12 nm with a standard deviation of 3.8 nm. EBSD analysis revealed a preferential texture of [110] normal to the surface of the metal. This data implied that lattice matching between the oxide and the underlying metal did not occur, therefore, the observed preferential growth direction is independent of the underlying crystal orientation. Crown Copyright (C) 2016 Published by Elsevier Ltd. All rights reserved.