JOURNAL OF MATERIALS SCIENCE-MATERIALS IN ELECTRONICS
卷 31, 期 21, 页码 18336-18343出版社
SPRINGER
DOI: 10.1007/s10854-020-04335-1
关键词
-
类别
资金
- National Natural Science Foundation of China [51677045]
- Fundamental Research Foundation for University of Heilongjiang Province [LGYC2018JC023]
The flexible energy storage film based on PVDF matrix has very extensive application. The electrical properties of PVDF composite films doped by nanometer MnO(2)was studied in this research, and the influences of MnO(2)content on dielectric constant, breakdown strength and energy storage properties were systematic investigated. The results indicated that using MnO(2)as fillers is an effective approach to improve the dielectric constant and breakdown strength of PVDF matrix composites. The dielectric constant is 18.1 and the breakdown electric field is 100 kV/mm when the content of MnO(2)is 10 wt%. In addition, both large energy storage density (1.67 J/cm(3)) and high energy storage efficiency (81.9%) are obtained in composite film with 10 wt% MnO2. The enhancement of dielectric constant and energy storage efficiency are due to the ionic polarization of MnO(2)under applied electric field. Moreover, the effect of MnO(2)on electron trapping improves the breakdown strength and energy storage density of MnO2/PVDF composite films. This work provides a feasible route for designing flexible composites with excellent energy storage performance.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据