The corrosive-cracking behavior of two types of reinforced concrete accelerated by a potentiostat and sustained compressive load was studied. The corrosion-rate function of steel bar in reinforced concrete based on electric-current evolution and the critical-cracking model of reinforced concrete considering the compressive load influence parameter were established. Subsequently, the interaction effects among compressive load, corrosion solutions, and materials on the corrosive cracking of reinforced concrete were proposed. The microstructures of corroded steel bar in seawater and compound solution were observed by SEM. Results showed that under the accelerated potentiostatic condition, there was interaction effect between compressive load and corrosive-ion attack on reinforced concrete. The compressive load had a threshold value for corrosion rate of steel bar and could increase the lateral tensile strength of reinforced concrete. Seawater and compound solution (1% NaCl + 0.5% MgSO4) could result in the increment of the critical compressive load, and decrease the lateral tensile strength of reinforced concrete. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据