CONSTRUCTION AND BUILDING MATERIALS
卷 126, 期 -, 页码 313-320出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2016.09.041
关键词
Repairing materials; B-MgO; Setting time; Compressive strength; Water resistance; Micro structure
资金
- National Natural Science Foundation of China [21276264, U1407104, U1507120]
- Natural Science Foundation of Qinghai Province [2015-ZJ-949Q]
Magnesium potassium phosphate cement (MKPC) incorporated with slag was prepared from the byproduct boron-containing magnesium oxide (B-MgO) from the production of Li2CO3 from salt lakes. The influence of the slag content on the setting time, compressive strength, water resistance and seawater corrosion resistance of MKPC was investigated. The composition and microstructure of MKPC were also studied in detail. The results demonstrate that the setting time of MKPC increases with increasing slag content. The compressive strength at 3 h and 28 d of MKPC specimens with 20 wt% slag can reach approximately 35 MPa and 60 MPa, respectively. Moreover, slag significantly improves the water resistance and the seawater corrosion resistance of MKPC. The properties of MKPC incorporated with 20 wt% slag indicated that it met the requirements for rapid repairing materials. (C) 2016 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据