composites; flame retardance; grafting; polyimides
资金
- National Natural Science Foundation of China [51873005, 21875015]
The integrated-functional additive of DOPO-MWCNTs in PA6 improved flame retardancy and antistatic properties significantly by forming an electric network and controlling severe dripping during burning. The network strengthened char structure and reduced heat and smoke release, with CO release cut by about half in CONE test.
In order to improve the flame retardancy and antistatic properties of polyamide 6 (PA6) at as low amount of additives as possible, an integrated-functional additive was synthesized by 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) and multiwalled carbon nanotubes (MWCNTs). The results showed 2 wt% of DOPO-MWCNTs distributed in PA6 formed an electric network and decreased volume resistivity sharply to 3.1 x 10(8) omega cm. In other words, it helped PA6 to get to the percolation threshold of semiconductor. By using of 3 wt% DOPO-MWCNTs, the severe dripping in burning of PA6 was almost controlled. The possible reason was also ascribed to the network formed by evenly dispersed DOPO-MWCNTs, which strengthened the char structure and held severe dripping of PA6. As a result, the heat and smoke release were also suppressed obviously. The most important is that CO release was about half cut in CONE test.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据