JOURNAL OF ALLOYS AND COMPOUNDS
卷 835, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2020.155444
关键词
Metal matrix composites; Powder metallurgy; Sintering; Microstructure; Wear testing
资金
- National Natural Science Foundation of China [51772081, 51837009, 51577158]
- Natural Science Foundation of Sichuan Province [2018JY0278]
- Industry-University-Research Cooperation Project of AECC [HFZL2018CXY003-4]
- Major Science and Technology Projects of Changsha City [kq1804010]
Obtaining good affinity between graphene and copper in copper-graphene composites is the key to make full use of the good anti-wear ability of graphene. Copper-graphene nanoplatelets (Cu-GNPs) composites were prepared by ball-milling and hot pressed sintering with the addition of a small amount of cobalt to form intact graphene/cobalt/copper interfaces. The microstructural characterization shows that the GNPs are uniformly distributed on the grain boundaries of copper grains. The cobalt here acts as binder, bringing graphene and copper together efficiently. Benefiting from the unique structural design, Cu-GNPs composite doped with 0.25 wt % cobalt exhibits improved anti-wear performance with a stable friction coefficient of 0.246 and a small volume wear rate of 8.3 x 10(-5) mm(3)/(N.m) (20% of that of pure copper composite). Excessive cobalt causes a significant increase of the structural defects in graphene and the formation of amorphous carbon, resulting in degradation of friction properties. (C) 2020 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据