INDUSTRIAL & ENGINEERING CHEMISTRY RESEARCH
卷 59, 期 40, 页码 18106-18114出版社
AMER CHEMICAL SOC
DOI: 10.1021/acs.iecr.0c03318
关键词
-
资金
- National Natural Science Foundation of China [51503216, 51672287]
- Natural Science Foundation of Zhejiang Province of China [LQ16E030003]
Nitrogen-containing porous carbon fibers with a large BET surface area (919-1625 m(2)/g) and pore volume (0.429-0.772 cm(3)/g) were developed from polyimide fiber, which was treated in the presence of potassium carbonate by one-step simultaneous carbonization/activation. The effect of carbonization temperature on the porous and chemical structure was monitored. The nitrogen contents of activated carbon fibers decreased with the treatment temperature, which varied in a range of 1.23-2.76 wt %. Compared with the unactivated fiber, the activated ones showed more ultramicropores with a volume of more than 0.279 cm(3)/g. An optimal activated sample exhibited an excellent CO2 uptake of 5.0 mmol/g at 1 bar and 25 degrees C, with an acceptable Henry's CO2/N-2 selectivity of 24. The ultramicropore played a predominant effect on the CO2 uptake capacity, while the nitrogen functionalities played a predominant effect on the CO2/N-2 selectivity.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据