FATIGUE & FRACTURE OF ENGINEERING MATERIALS & STRUCTURES
卷 43, 期 10, 页码 2455-2475出版社
WILEY
DOI: 10.1111/ffe.13316
关键词
crack growth; elevated temperatures; ultrasonic fatigue testing system; very high cycle fatigue
资金
- German Research Foundation (DFG) [169148856]
The fatigue life of cast steel G42CrMo4 in two different heat treatment conditions was investigated at room temperature (RT), 473 K and 773 K up to the range of very high cycle fatigue (VHCF), that is, 10(9)cycles. The fatigue life is determined by casting defects, the hardness of the steel matrix and by temperature. Fatigue life data were discussed in correlation with crack-initiating defects analysed on fracture surfaces. The SN curves obtained at RT and at 473 K show a large scatter. However, the SN curve at 773 K exhibits a larger slope parameter and a significantly reduced scatter. It is shown that the fatigue behaviour of the cast steel G42CrMo4 changes from 473 to 773 K in the range of VHCF. The fatigue lives of the specimens tested at 773 K were described with a crack growth model.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据