ELECTROCHEMISTRY COMMUNICATIONS
卷 119, 期 -, 页码 -出版社
ELSEVIER SCIENCE INC
DOI: 10.1016/j.elecom.2020.106813
关键词
Hydrogen; Monovalent Mg; Corrosion; Mg17Al12; Raman; Mg+/MgH+
资金
- Lebanese University
- AZM & SAADE Association
Previous investigations (DFT calculations) showed that hydrogen atoms adsorption and H-2 desorption can occur on MgO and Al2O3 and that H atoms can diffuse on Mg and Al surfaces. However, these three simultaneous actions, i.e. H adsorption, H diffusion and H-2 desorption, have not been experimentally proved. In this paper, we propose a mechanism of formation of H-2 during the corrosion of an intermetallic compound Mg17Al12 in 3.5 wt. % NaCl aqueous solution based on in situ Raman spectroscopy analysis. We found that, through the passivation zone (e.g. E varying from the open circuit potential (OCP) to +100 mV/OCP), the oxide layer is destroyed in favor of the appearance of Mg and H atoms. Moreover, the formed H atoms are adsorbed on the oxide surface and then diffuse on either the oxide surface or the unreacted metal surface where they recombine forming H-2. In situ Raman measurements during anodic polarization experimentally prove, for the first time, the formation of a reaction intermediate which weakens the H-H bond. The obtained results explain the mechanism of hydrogen production under anodic polarization of the intermetallic compound at normal conditions of temperature and pressure.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据