CONSTRUCTION AND BUILDING MATERIALS
卷 259, 期 -, 页码 -出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.conbuildmat.2020.119768
关键词
Shrinkage-compensating concrete; High-performance expansive agent; Fiber; Workability; Crack resistance; Permeability; Chloride penetration
资金
- National Key Research and Development Plan, China [2018YFC0705700]
- National Natural Science Foundation of China [51778462, 51908416]
- Shanghai Pujiang Program [19PJ1409500]
The effect of hybrid CaO- and ettringite-based expansive agents (HCSA) on the mechanical properties and durability of shrinkage-compensating concrete (SHRCC) is not well established. In this paper, SHRCC specimens were prepared incorporating with a high-performance calcium sulfoaluminate- hydrate calcium hydroxide expansive agent (HCSA) and three different types of fibers, i.e., polypropylene fiber (PP), polyvinyl alcohol fiber (PVA), and cellulose fiber (CF). The first part of the experimental program included material tests of the slump, compressive strength, restrained expansion ratio, early crack resistance, permeability and chloride penetration of SHRCC. The test results indicated that the HCSA-based SHRCC exhibited good workability, early crack resistance and durability. It is suggested that HCSA with a dosage of 7% - 8% of the weight of binder materials provided favorable shrinkage compensation and early crack resistance and had negligible impacts on the slump and compressive strength of the SHRCC. Although the content was low (approximately 0.7% by volume), PP fibers effectively improved the early crack resistance of the SHRCC. Adequate moist curing was also required to retain acceptable permeability and chloride penetration of the SHRCC. The second part of the experimental program involved tests on small-scale concrete basement slabs, which verified the effects of the expansive agent and fibers on the crack resistance of SHRCC at the component level. (C) 2020 Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据