期刊
CERAMICS INTERNATIONAL
卷 47, 期 4, 页码 4681-4687出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2020.10.035
关键词
Highly transparent Y2O3; Powder processing; Milling; Optical properties; Hot-pressing
资金
- National Research Foundation (NRF) of MSIT [NRF-2020M3H4A3106003]
- Industrial Technology Innovation Program of MOTIE, Republic of Korea [PN: 20000343]
- Korea Evaluation Institute of Industrial Technology (KEIT) [20000343] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
- National Research Foundation of Korea [2020M3H4A3106003] Funding Source: Korea Institute of Science & Technology Information (KISTI), National Science & Technology Information Service (NTIS)
This study presents highly transparent Y2O3 ceramics fabricated at 1500 degrees C without HIP treatment, achieving in-line transmittance levels of 77% and 84% at wavelengths of 400 and 1100 nm. The influence of ball size during grinding on the optical properties of the samples was demonstrated for the first time. Results showed that using 2 mm balls led to the best combination of fine-grained structure and pore-free microstructure with optimal in-line transmittance for Y2O3 ceramics.
In this study, we report highly transparent Y2O3 ceramics fabricated by hot-pressing only at 1500 degrees C without a HIP treatment, featuring in-line transmittance levels of 77% and 84% at a wavelength of 400 and 1100 nm, respectively with the grain size suppressed to 710 nm. The effect of the ball size during the grinding of Y2O3 powders on the correlation between the thus-prepared Y2O3 powders and the optical properties of the hot-pressed samples is demonstrated for the first time. With a decrease in the diameter of the ZrO2 balls from 5 mm to 1 mm, the milling efficiency was enhanced and admirable transparency of Y2O3 was attained at a short milling time. However, several micron-sized pores remained in the transparent specimens prepared with 1 mm balls, originating from the inhomogeneously packed region of the green body. Finally, the 2 mm was found to be optimum for obtaining a fine-grained and pore-free microstructure with the best in-line transmittance of Y2O3 ceramics.