期刊
APPLIED PHYSICS A-MATERIALS SCIENCE & PROCESSING
卷 126, 期 9, 页码 -出版社
SPRINGER HEIDELBERG
DOI: 10.1007/s00339-020-03908-5
关键词
Zn alloying degree; 5083 aluminum alloy; Dislocation strengthening; Corrosion resistance
资金
- Zhenjiang Key Research and Development Program [SGY20180110115]
The influence of three kinds of alloy adding 0.3-1.8 wt% Zn on the mechanical properties and corrosion resistance of medium Mg content 4.0-4.5 wt% (5083 type) hot rolled alloy was investigated. The results showed that the addition of Zn content could further dissolve the second phases into the matrix. The hardness and tensile strength were reduced when annealing at 250 degrees C x 2 h. The mechanical behavior of the alloys showed a tendency that increases first and then decreases and the peak reached its maximum when 1.6 wt% Zn is added at both annealed and unannealed states. Through quantitative analysis, the improvement of mechanical properties mainly comes from dislocation strengthening and Al-Mg-Zn ternary strengthening phases. Meanwhile, with the increase of Zn content, the intergranular corrosion (IGC) of the alloy improved greatly after annealing at 250 degrees C x 2 h. The electrochemical corrosion potential (ECP) of the alloys increased first and then decreased.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据