Effect of microstructure change on permeability of flax-fiber reinforced silty clay soaked with zinc-ion solution

With the application of fiber-reinforcement technology, the mechanical properties of silty clay are improved with fiber reinforcement. However, the variation of permeability coefficient and other parameters of flax-fiber reinforced silty clay have not been sufficiently studied. In this study, the permeability of flax-fiber reinforced silty clay soaked with zinc-contaminated solution under different osmotic pressure was tested by a flexible-wall permeameter, and the effects of zinc-ion concentration and confining pressure on the permeability of flax-fiber reinforced silty clay were studied. Genius XRF was employed to detect the types and quantity of metal elements in the specimens, thereafter, the reasons for the change of permeability were explained from chemical and microscopic perspective. The results showed that the permeability coefficient of flax-fiber reinforced silty clay decreased significantly with the increase of zinc-ion concentration in a low concentration (about 1-10 mg L-1). While in a high concentration (about 100 mg L-1), the permeability coefficient of flax-fiber reinforced silty clay changed little with the increase of zinc-ion concentration. While the flax-fiber reinforced silty clay was not soaked with zinc-ion solution, the permeability coefficient of the specimen increased with the increase of confining pressure. However, when the flax-fiber reinforced silty clay was soaked with zinc-contaminated solution, the permeability coefficient first decreased and then tended to be constant with the increase of confining pressure. With the increase of confining pressure, the porosity of flax-fiber reinforced silty clay decreased, and with the increase of zinc-ion concentration, the porosity of flax-fiber reinforced silty clay first increased and then decreased.