期刊
SENSORS AND ACTUATORS B-CHEMICAL
卷 316, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.snb.2020.128206
关键词
NH3 sensor; BiVO4; Ag doping; Oxide reference electrode; La9.95K0.05Si5Al1O26.45
资金
- Natural Science Foundation of China [51872090, 51672080, 51472073, 51772097]
- Natural Science Key Foundation of Hebei Province of China [E2017209260]
- Natural Science Foundation of Hebei Province of China [E2017209079, E2016209359, E2016209333]
Mixed potential NH3 sensors with La9.95K0.05Si5AlO26.45 (LKSAO) as the solid electrolyte and Bi1-xAgxVO4-delta as the sensing electrode (SE) were developed. Bi1-xAgxVO4-delta was produced by solid state reaction and then characterized by XRD, XPS, SEM and EDS. As revealed from the results, The BiVO4 samples exhibit an unchanged crystalline structure after Ag doping molar amount x <= 0.2, accompanied by the growth of the particle. The sensor based on Bi1-xAgxVO4-delta exhibit the noticeably enhanced sensing performance to NH3 in contrast to the sensor using BiVO4, including its larger response potential (Delta V) and higher sensitivity. For instance, the sensors based on BiVO4 and Bi0.8Ag0.2VO4-delta at 400 degrees C exhibit the sensitivities of -28.1 and -77.3 mV/decade, respectively. Nevertheless, by Ag doping, there is no effective improvement of the anti-interference ability of the sensor against NO and NO2. To address the mentioned problem, CuO, NiO and La0.8Sr0.2MnO3 (LSM) were used as reference electrodes (RE). As suggested from the results, using CuO and NiO as the reference electrodes can obviously reduce the cross-sensitivity of the sensor to NO and NO2, whereas the sensitivity slightly decrease.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据