pH; CaTi2O5; Solvothermal method; Photocatalytic properties
资金
- National Natural Science Foundation of China [51502119]
- Jiangxi Major Natural Science Foundation [20152ACB21022, 20161BBH80048]
The study revealed that pH values have a crucial effect on the crystal phase and shape evolution of CaTi(2)O(5) samples. The CaTi(2)O(5) sample prepared at pH of 5.2 exhibits efficient light harvesting and excellent crystallinity.
CaTi(2)O(5)was selectively prepared by a solvothermal process without template and surfactant. The phase of the as-prepared samples was determined by X-ray diffraction (XRD). The microstructure was characterized by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Results found that pH values had a crucial effect on the crystal phase and shape evolution of the samples. CaTi(2)O(5)sample prepared at pH of 5.2 shows high efficient light harvesting, large surface area and crystallinity. Moreover, CaTi(2)O(5)shuttle-like sample shows good photocatalytic activity against methyl orange due to its longer and thinner shuttle-like morphology and high crystallinity, enhanced light harvesting and large surface area. The photocatalytic rate of CaTi(2)O(5)shuttle-like structure reaches 0.1988 min(-1)for 25-min methyl orange degradation under the ultraviolet light irradiation and displays an excellent photostability with a degradation efficiency of 0.1952 min(-1)after four cycles.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据