Flax fabric; Carbon fabric; Hybrid composites; Hybrid effect
资金
- National Natural Science Foundation of China [51478145]
- Chinese MIIT Special Research Plan on Civil Aircraft [MJ-2015-H-G-103]
A hybrid of flax and carbon fibers was considered as an effective way to enhance the mechanical and hydrothermal resistance of flax-reinforced polymer composites. In this study, hybrid composites based on three layers of cross-ply flax fabrics, two layers of unidirectional carbon fabrics, and an epoxy resin were investigated in terms of the tensile, three-point bending, impact, and water absorption properties. The flax fabric reinforcement of the hybrid composites contributed to an improvement in the toughness, whereas the carbon fabric contributed to an improvement in their hydrothermal resistance and overall strength and stiffness. The hybrid composites with carbon fibers on the surface (CFFFC) exhibited brittle failure in the tensile test, whereas those with alternating layers (FCFCF) exhibited greater plastic deformation. In addition, the failure strain of the CFFFC samples showed a negative hybrid effect, whereas that of the FCFCF samples improved 63.5% compared with that of carbon-fiber-reinforced polymer composites. A positive hybrid effect on the impact performance of hybrid reinforced epoxy composites containing the unidirectional carbon fabric and cross-ply flax fabric was observed. At 40 degrees C and 80% relative humidity, the diffusion rate of water molecules in the FCFCF samples was 16 times that in the CFFFC samples.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据