MATERIALS SCIENCE AND TECHNOLOGY
卷 36, 期 14, 页码 1523-1533出版社
TAYLOR & FRANCIS LTD
DOI: 10.1080/02670836.2020.1799137
关键词
Mechanical behaviour; embrittlement; carbides; hardening; selective laser melting; superalloy
资金
- National Natural Science Foundation of China [NSFC51905249]
- Natural Science Foundation of JiangXi Province [20192BAB216020]
- Innovation Fund Designated for Graduate Students of Jiangxi Province [YC2018-S373]
Mechanical behaviour of Haynes 230 and Inconel 625 manufactured by selective laser melting (SLM) has been experimentally investigated in 870(o)C. Significant embrittlement of SLM Inconel 625 was found, accompanied by hardening behaviour during the test. Moreover, due to inhomogeneous grain deformation, the hardness dispersion of the two SLM alloys increased significantly. Employing a systematic research with scanning electron microscopy and energy-dispersive spectrometer, intergranular cracking of two SLM alloys can be observed from the surface cracks and fracture appearances, respectively. In addition, carbides along grain boundaries of the two nickel-based superalloys were found and affected the strength of the grain boundary at 870(o)C. Therefore, it resulted in different fracture mechanisms.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据