cytotoxicity; mechanical strength; porosity; scaffold
资金
- Vicerrectoria de Investigacion y Extension at Universidad Industrial de Santander (UIS) [1824]
Reticulated vitreous carbon (RVC) foams have shown favorable biocompatibility and the potential to support osteoblastic adhesion. In this work, RVC foams were fabricatedviatemplate route, using a low-cost sucrose-based resin. The effect of several process parameters, such as template porosity (cell size between 500 and 1400 mu m) and carbonization conditions, were studied. The resulting RVC foams displayed highly interconnected porosity (> 85%) with controllable cell size, bone-like morphology, and compressive strength of 0.06-0.26 MPa. The results suggested that the decrease in the cell size of the sacrificial sponge, the increase in the thickness of the sponge cell ligaments, and the carbonization temperature of 1500 degrees C, contributed to the enhancement of the mechanical response of the fabricated scaffolds. Finally, cytotoxicity and cell adhesion assays were carried out using normal human osteoblasts as a preliminary assessment of the cytocompatibility of the synthesized RVC foams. Although the mechanical strength of these foams could still be improved, these results contribute towards the development of low-cost bioactive scaffolds that resemble the morphological properties of the trabecular bone.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据