Evaluation of bond strength of resin cement to Er:YAG laser-etched enamel and dentin after cementation of ceramic discs

The purpose of this study was to investigate the shear bond strength (SBS) of ceramic discs luted to differently etched enamel and dentin surfaces. Occlusal surfaces of 64 carious-free human molars and vestibule surfaces of 64 first maxillary incisors were ground to get flat superficial dentin and flattened enamel respectively. After generating 4 groups according to the surface etching method (37% orthophosphoric acid, Er:YAG laser-contact handpiece/scanning handpiece (1 or 2 times of scanning)), ceramic discs were luted to the surfaces with adhesive resin cement (Variolink N, Vivadent Ets., Schaan/Liechtenstein). After etching and cementation, thermocycling of 5000 cycles (Sd Mechatronik Gmbh, Feldkirchen-Westerham, Germany) and SBS test (Servopulser EHFFD1; Shimadzu, Kyoto, Japan) were performed respectively. The surface morphologies of 2 specimens, etched enamel and dentin, prepared for each group were examined with SEM analysis. Failure modes were determined under a USB digital microscope. Data were analyzed with one-way analysis of variance (ANOVA) and Tukey HSD test (alpha = 0.05). SBS values in dentin surfaces showed statistically significant differences (p < 0.05) among tested groups. The highest SBS among dentin groups was determined in the group which had 2 times etching by Er:YAG laser (11.42 MPa) by a scanning handpiece. No statistical differences were observed in the other dentin or enamel groups. Laser etching seems to be a viable alternative to acid etching on both enamel and dentin surfaces while double etching of dentin with a scanning handpiece can improve the adhesion.

Automated summary

The study aimed to investigate the shear bond strength of ceramic discs luted to differently etched enamel and dentin surfaces. It found that double etching of dentin with Er:YAG laser can improve adhesion. Laser etching appears to be a viable alternative to acid etching on both enamel and dentin surfaces.