JOURNAL OF THERMAL ANALYSIS AND CALORIMETRY
卷 146, 期 3, 页码 1371-1381出版社
SPRINGER
DOI: 10.1007/s10973-020-10131-0
关键词
Polyacrylamide; Cationicity; Methacryloyloxyethyl trimethylammonium chloride; Thermal decomposition; TG-FTIR-MS; Mechanism
The thermal decomposition behavior of polyacrylamide poly (methacryloyloxyethyl trimethylammonium chloride-acrylamide) (P(DMC-AM)) was studied using TG and DSC, revealing that an increase in cationicity led to higher thermal stability for P(DMC-AM). The evolved gases during degradation were analyzed using TG coupled with FTIR and MS, and a possible thermal composition mechanism was proposed and validated, providing useful information for expanding innovative applications.
The thermal decomposition behavior of polyacrylamide poly (methacryloyloxyethyl trimethylammonium chloride-acrylamide) (P(DMC-AM)) was studied by means of TG and DSC under nitrogen atmosphere at temperature range of 323.15-823.15 K. The effect of cationicity on thermal stability was discussed. The TG/DSC curves indicated that the decomposition process of P(DMC-AM) included three steps, and an increase in cationicity resulted in a slightly increased decomposition temperature and decomposition enthalpy, indicating a higher thermostability for P(DMC-AM). Furthermore, the evolved gases during the degradation were analyzed simultaneously via TG coupled with FTIR and MS. The possible thermal composition mechanism was proposed and validated by calculating the bond orders. The results from this study might supply useful message for expanding innovative application.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据