Microstructure, tensile properties and thermal stability of AlMgSiScZr alloy printed by laser powder bed fusion

期刊

JOURNAL OF MATERIALS SCIENCE & TECHNOLOGY
卷 69, 期 -, 页码 200-211

出版社

JOURNAL MATER SCI TECHNOL
DOI: 10.1016/j.jmst.2020.08.033

关键词

Laser powder bed fusion; AlMgSiScZr alloy; Microstructure; Tensile behavior; Thermal stability; Phase evolution

向作者/读者索取更多资源

The new generation of Sc and Zr modified Al alloys has attracted wide attention in the aerospace industry due to their excellent mechanical properties and thermal stability. The LPBF-processed AlMgSiScZr alloy exhibits high tensile strength and good thermal stability, making it suitable for replacing some titanium alloys in aerospace applications.
The new generation of Sc and Zr modified Al alloys has been attracted wide concerns in aerospace industry, owing to the excellent mechanical performances and superior thermal stability than other normal Al alloys. By microalloying with Sc and Zr, the A13(Sc, Zr) particle forms as the grain refiner during the solidification, which is extremely beneficial for the laser powder bed fusion (LPBF) processed Al alloys. In this study, a new type A1-14.1Mg-0.475i-0.315c-0.17 Zr alloy was additively manufactured by LPBF, and the microstructure, tensile properties and thermal stability were studied in detail. By using a single melt67 degrees scanning strategy, the LPBF-processed specimen with a relative density of 99.4 % and tensile strength of 487.7 MPa was obtained at 160 W-200 mm/s. And this AlMgSiScZr alloy can still exhibit an excellent tensile strength of 393.9 MPa at a moderate temperature of 473 K. After the aging treatment, the tensile properties further increased due to the precipitate hardening of Mg2Si and A13( Sc, Zr), and the maximum value (580 MPa) was reached at an aging time of 10 h. The average crystal size was almost unchanged after aging treated at 325 degrees C and 24 h, indicating this AlMgSiScZr alloy has an improved thermal stability. The AlMgSiScZr alloy is recommended to substitute some particular titanium alloys in aerospace field afterwards. (C) 2021 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.7
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据