Grain boundary migration; Orientation dependence; Texture; Nano-grain; Copper
资金
- Chinese Ministry of Science and Technology [2017YFA0204401, 2017YFA0700700]
- Chinese Academy of Sciences [zdyz201701]
Tensile tests on gradient nanograined copper samples reveal that GBM is more pronounced in grains with higher Schmid factors, leading to changes in grain boundary angles.
Tensile tests were carried out on gradient nanograined copper samples to investigate the grain orientation dependence of mechanically induced grain boundary migration (GBM) process. The relationship between GBM and the orientations of nanograins relative to loading direction was established by using electron backscatter diffraction. GBM is found to be more pronounced in the grains with higher Schmid factors where dislocations are easier to slip. As a result, the fraction of high angle grain boundaries decreases and that of low angle grain boundaries increases after GBM. (C) 2021 Published by Elsevier Ltd on behalf of The editorial office of Journal of Materials Science & Technology.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据