Layered solidification technology; Electron beam smelting; Cooling rate; Microsegregation; Melt superheating treatment
资金
- National Key Research and Development Program of China [2017YFA0403804]
- National Natural Science Foundation of China [91860123]
- Fundamental Research Funds for the Central Universities [DUTl8ZD206]
- China Post-doctoral Science Foundation [ZX20190056]
Based on the principle of additive manufacturing in a layer-by-layer manner, a new electron beam smelting layered solidification technology (EBS-LST) was curried out to fabricated Inconel 718 superalloy. The microsegregation coefficient and the redistribution were calculated. A well-recognized model associated with secondary dendrite arm spacing was used to investigate the cooling rate during the solidification. The distribution of the surface temperature of the molten pool during EBS-LST was calculated based on the Gaussian distribution. The results show that there is a dendritic-cellular interface with a width of 400 mu m between the layers, and the secondary dendrite arm spacing approximates 23 mm. The value of microsegregation coefficient of Nb, Mo and Ti is approximately 1.97, 1.52 and 1.13, respectively. Its solute distribution is more uniform than conventional processes, which attributed to the high cooling rate of the solidification process. (c) 2020 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据