期刊
APPLIED CATALYSIS B-ENVIRONMENTAL
卷 271, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.apcatb.2020.118941
关键词
Co-based mixed oxide catalyst; Volatile organic compound; Electrodeposition method; Porous nanosheet structure; Catalytic oxidation
资金
- Jiku Chemical Co. Ltd.
- Japan
- China Scholarship Council (CSC), P. R. China
Cerium (Ce) modified cobalt (Co)-based (Co-Ce) mixed oxide catalysts were electrodeposited on nickel foam (NF) with different Co/Ce molar ratios and directly used for the catalytic oxidation of toluene. Physicochemical properties of the obtained Co-Ce/NF catalysts were obtained by SEM, XRD, TEM, H-2-TPR, O-2-TPD and XPS techniques. It was found that the Co-Ce mixed oxide with a well nanosheet structure could be uniformly deposited on NF by adjusting the Co/Ce molar ratio in the initial solution for electrodeposition. H-2-TPR analysis indicated that Ce doping improved the reducibility of Co-Ce/NF catalyst due to the synergistic effect between Co and Ce. In the toluene catalytic oxidation, the 10Co-Ce/NF catalyst prepared with a molar ratio of Co/Ce at 10 in the initial solution achieved the best catalytic performance among all the catalysts with a complete toluene conversion temperature of 268 degrees C and CO2 selectivity of 100 %. This can be contributed to the superior physiochemical properties of uniform nanosheet structure, rich surface and lattice active oxygen species at low temperatures, high content of Co3+ active species with high oxygen vacancies and Ce4+/Ce3+ redox couples in the catalyst. In addition, the 10Co-Ce/NF catalyst exhibited long-term stability in the presence of water vapor. It is expected that such a time-saving electrodeposition method could provide a promising way to prepare highly active and stable transition metal based catalysts for the oxidation of VOCs.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据