期刊
MOLECULAR CATALYSIS
卷 486, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.mcat.2020.110879
关键词
Toluene; Catalytic oxidation; Ag nanoparticles; CeO2; Copper nanowire; Electrodeposition method
资金
- Jiku Chemical Co. Ltd.
A novel catalyst with special three-dimensional structure was prepared for the catalytic oxidation of toluene using a three-step electrochemical process, in which copper nanowires (CNWs) were generated on the surface of three-dimensional Cu foam (CF) by an electro-oxidization process at first and then, CeO2 was uniformly coated on the CNWs by a unipolar pulse electro-deposition (UPED) method and finally highly dispersed Ag nanoparticles were embedded on the surface of CeO2 using a constant voltage electrodeposition method. It is found that the suitable Ag loading amount effectively enhanced the low-temperature reducibility, the generation of oxygen vacancies, and distribution of surface acid sites, which are favorable to the catalytic oxidation of toluene. Especially, the obtained 80Ag-CeO2 @CNWs/CF catalyst with an electrodeposition time of 80 s for Ag loading exhibited the best catalytic activity with the T-10 , T-50 and T-90 of toluene conversion at 222, 240 and 256 degrees C, respectively. Long-term stability tests with and without water vapor further indicated that the 80Ag-CeO2@CNWs/CF catalyst had good stability and water resistance ability during the catalytic oxidation of toluene. It is expected that the present electrodeposition method could be a promising way to prepare highperformance catalysts for the catalytic oxidation of VOCs.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据