Preparation and properties of endothermic functional ceramics with iron tailings as raw materials

期刊

MATERIALS RESEARCH EXPRESS
卷 7, 期 5, 页码 -

出版社

IOP PUBLISHING LTD
DOI: 10.1088/2053-1591/ab8b8a

关键词

iron tailings; functional ceramics; endothermic performance; solar energy

资金

  1. Hebei Province Giant Plan Innovation Team

向作者/读者索取更多资源

The present work attempts to utilize iron tailings as the main raw materials for preparation of functional ceramics as a means of resource utilization. A new type of endothermic functional ceramics, which can be used in the field of solar energy, was prepared via semi-dry pressing followed by pressureless sintering. The results show that the functional ceramics made of 68 wt% iron tailings, 26 wt% iron ore, 3 wt% alumina, 1 wt% potash feldspar and 2 wt% kaolin, sintered at 1185 degrees C exhibited the best overall performance. Visual observation reveals that there were no cracks on the surface of the samples even after 20 cycles of intense thermal shock. Other attributes could be summarized as follows: Infrared emissivity in mid-infrared region: 0.85; thermal conductivity at 500 degrees C: 2.066 W/(mK); flexural strength: 119.03 MPa. XRD analysis indicates that the main crystalline phases in the samples are augite, magnetite and a small amount of hematite. An increase in the proportion of iron oxide contributed to lower melting temperature of the functional ceramics, deepen color, promote densification and increase infrared emissivity. In short, the introduction of iron tailings improves the thermal and physical properties to a certain extent.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据