期刊
CRYSTALS
卷 10, 期 3, 页码 -出版社
MDPI
DOI: 10.3390/cryst10030207
关键词
Cu1; 5Cr0; 1Si alloy; equal channel angle pressing (ECAP); electron back-scattered diffraction (EBSD); microstructure texture
资金
- National Natural Science Foundation of China [51861022, 51261016]
The evolutions of the microstructure and its effect on the mechanical and electrical conductivity properties of Cu1.5Cr0.1Si alloy after equal channel angle pressing (ECAP)-C path deformation and aging treatment have been investigated using scanning electron microscopy (SEM), X-ray diffraction (XRD), and electron back-scattered diffraction (EBSD). It was found that after the ECAP-C deformation at room temperature, with an extension of aging time, the strong (111) macro orientation formed in the Cu1.5Cr0.1Si alloy. The ultrafine crystals formed by ECAP and the rich chromium phase precipitated along grain boundaries during the aging process greatly improved the material strength. After aging at 350 degrees C for 4 h, the tensile strength, elongation, and conductivity reached 528 MPa, 15.27%, and 78.9% IACS, respectively. The fracture mode of the alloy was ductile fracture. The steady-oriented {111} texture was beneficial to improving the conductivity of the material.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据