关键词
CsPbBr; (3) perovskite nanocrystals; recombination process; solution-processed; surface passivation
All-inorganic lead halide perovskites with good surface morphology show substantial prospect for optoelectronic devices. However, the anion exchange of coordinated alkylamine ligands (e.g., oleic acid and oleylamine) can detach ligands and induce more interface trap sites, subsequently to reduce device performance. In this paper, therefore, a simple solution-processed route is presented to synthesize quasi coreshell CsPbBr(3)formamidinium iodide (FAI = CH(NH2)(2)I) colloidal quantum dots (CQDs), and then it is applied as the active layer for photodetectors by finely controlling the ligands exchange. The presence of FAI = CH(NH2)(2)I on CsPbBr3 is confirmed by Fourier transform infrared spectroscopy. As a result, the photodetector ITO/ZnO (100 nm)/CsPbBr3 (150 nm)/Au show an enhanced specific detectivity over 10(13) Jones with a responsivity of 19 A W-1 under 3 mW cm(2) 405 nm illumination at 1.5 V. The experimental data show that the enhanced device performance is due to the improved crystallinity and less surface defects of CsPbBr3 CQDs, as the result of less alkylamine ligands is detached during its FAI passivation, thus the charge carriers' mobility of the film is improved. Therefore, it provides a promising way for high-performance solution-processed all-inorganic CsPbBr3 based optoelectronic devices.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据