Rapid Synthesis of Elastomers and Thermosets with Tunable Thermomechanical Properties

Rapid, solvent-free synthesis of poly(1,4-butadiene) in ambient conditions is demonstrated by frontal ring-opening metathesis polymerization (FROMP) of 1,5-cyclooctadiene (COD). Furthermore, cross-linked copolymers with a wide range of tunable properties are readily prepared by FROMP of mixtures of COD and dicyclopentadiene (DCPD). Specifically, glass transition temperature and tensile modulus are varied from -90 to 114 degrees C and 3.1 MPa to 1.9 GPa, respectively, by controlling the comonomer ratio. Copolymers with subambient glass transition temperature exhibit robust elastomeric behavior, with the ability to repeatedly recover from large elastic deformations. As a demonstration of the capability of this manufacturing strategy, gradient materials are fabricated in less than a minute with spatially controlled properties for multistage shape memory actuation. This simple yet powerful manufacturing strategy enables rapid synthesis of copolymers ranging from elastomers to thermosets with precise control over thermomechanical properties.