TRIP steel; medium-C steel; retained austenite; deformation temperature; mechanical stability
类别
资金
- National Science Center, Poland [2017/27/B/ST8/02864]
The temperature-dependent microstructural evolution and corresponding mechanical stability of retained austenite in medium-C TRIP-assisted 0.43C-1.45Mn-0.98Si-1Al-0.033Nb-0.01Ti steel obtained by thermomechanical processing was investigated using static tensile tests and microstructural studies. The light microscopy, image analysis, XRD diffraction and the Jaoul-Crussard analysis were applied to reveal relationships between microstructure and mechanical properties. Specimens were deformed in the static tensile tests in a temperature range of -20-140 degrees C. It was found that an increase in deformation temperature resulted in the reduced intensity of the TRIP effect due to the higher stability of retained austenite. An increase in the retained austenite stability along with a smaller grain size and a change from its blocky morphology to thin layers was also indicated. The impact of strengthening mechanisms at different temperatures was analyzed. The best combination of strength and ductility was obtained in the samples deformed at 20 and 60 degrees C, which is associated with the moderate work hardening in this temperature range. The Jaoul-Crussard analysis showed much less strengthening during the second phase of deformation at 100 and 140 degrees C due to the high stability of retained austenite. The higher C content in the investigated TRIP steel resulted in substantial volume fractions of retained austenite stable after completing deformation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据