期刊
MATERIALS
卷 13, 期 7, 页码 -出版社
MDPI
DOI: 10.3390/ma13071546
关键词
zirconia; microstructure; Vickers hardness; microwave sintering
This paper reports the improvement of microstructural and hardness properties of 3 mol% yttria-stabilized zirconia (3Y-TZP) ceramics with nano TiO2 powders (with 0, 0.9, 1.8, and 2.7 wt%) added using a low-temperature microwave-assisted sintering of 1250 degrees C. Even at such a low sintering temperature, all sintered samples had the main phase of tetragonal zirconia (t-ZrO2) without the appearance of the secondary monoclinic phase or TiO2 phase, and had high relative densities, larger than 95%. The grain growth was well developed, and the grain sizes were around 300-600 nm. The Ti and O elements appeared at the grain and grain boundary and increased with the increased nano TiO2 contents identified by the element analysis, although the TiO2 phase did not appear in the X-ray pattern. The Vickers hardness was in the range of 10.5 to 14.5 GPa, which first increased with increasing content till 0.9 wt% and then decreased. With citric acid corrosion treatment for 10 h, the Vickers hardness only decreased from 14.34 GPa to 13.55 GPa with the addition of 0.9 wt% nano TiO2 powder. The experiment results showed that 0.9 wt% nano TiO2 addition can improve the densification as well as the Vickers hardness under a low temperature of microwave-assisted sintering.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据