期刊
MATERIALS
卷 13, 期 7, 页码 -出版社
MDPI
DOI: 10.3390/ma13071529
关键词
clinker; heavy metal; solidification; Si-29 MAS NMR; Cr
类别
资金
- National KeyR&DProgram of China [2010ZX07319-002]
In order to reveal the solidification behavior of Cr in the cement clinker mineral phase, Si-29 magic-angle spinning nuclear magnetic resonance, X-ray diffraction, and scanning electron microscopy with energy-dispersive X-ray spectroscopy techniques were used to analyze the morphology and composition of the cement clinker mineral phase doped with Cr. The results showed that the addition of Cr did not change the chemical environment of Si-29 in the clinker mineral phase, and it was still an isolated silicon-oxygen tetrahedron. Cr affected the orientation of the silicon-oxygen tetrahedron and the coordination number of calcium, leading to the formation of defects in the crystal structure of the clinker mineral phase, by replacing Ca2+ into the mineral phase lattice to form a new mineral phase Ca3Cr2(SiO4)(3). Cr acted as a stabilizer for the formation of beta -C2S in the clinker calcination. As the amount of Cr increased, the relative content of C3S decreased and the relative content of C2S increased. Further, Cr easily dissolved in C2S, while it was not found in C3S. This study is conducive to further research on the mechanism of heavy metal solidification in cement clinker. Furthermore, it is important to evaluate the environmental risk of heavy metals in the process of sludge disposal through cement kiln and promote the utilization of sludge resources and the sustainable development of the cement industry.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据