ARABIAN JOURNAL OF CHEMISTRY
卷 13, 期 7, 页码 6044-6055出版社
ELSEVIER
DOI: 10.1016/j.arabjc.2020.05.004
关键词
AZ91D magnesium alloy; Distilled water; Corrosion; EIS; SEM
资金
- National Natural Science Foundation of China [51401151]
- Natural Science Foundation of Hubei [2018CFB525]
The corrosion of AZ91D magnesium alloy has received extensive attention due to the continuous expansion of its application field in recent years. However, the corrosion of AZ91D magnesium alloy in distilled water is relatively few. In this paper, the corrosion behavior of AZ91D magnesium alloy was studied in distilled water by electrochemical tests in combination with weight loss and surface analysis methods. The results indicated that the corrosion rate of AZ91D magnesium alloy increased with the increase of temperature and immersion time. The increase of the corrosion rate of AZ91D magnesium alloy with the increase of immersion time might be attrib-uted to the damage of the structure of corrosion product film by hydrogen evolution, significantly accelerating the anodic process of AZ91D magnesium alloy. It was interesting that, in distilled water, the EIS of AZ91D magnesium alloy excluded an inductive arc in the low frequency region, which indicated that there was no the adsorption and desorption of aggressive ions or the damage and repair of film. The corrosion product film of AZ91D magnesium alloy in distilled water was composed of a compact inner corrosion product film and a loose outer corrosion product film. (C) 2020 Published by Elsevier B.V. on behalf of King Saud University.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据