JOURNAL OF THERMAL SPRAY TECHNOLOGY
卷 29, 期 6, 页码 1508-1524出版社
SPRINGER
DOI: 10.1007/s11666-020-01028-3
关键词
additive manufacturing; cold spray; contour method; neutron diffraction; residual stress; titanium
资金
- CSIRO and its Active Integrated Matter Future Science Platform (AIM FSP)
In cold spray additive manufacturing (CSAM), the severe plastic deformation of the input powder particles leads to an accumulation of residual stresses, the magnitude of which is affected by process conditions. In the current study, the effects of traverse speed and powder feed rate on the residual stress state were investigated in commercially pure titanium cylinders produced by CSAM. Residual stress measurements were made in a grid pattern covering the 2D cross section using the KOWARI neutron diffractometer at ANSTO, Australia, and selected results were validated using the contour method. It was found that the thermal effect was dominant on the residual stress state generating a tensile state near the inner and outer surfaces of the cylinder walls while compressive residual stresses tend to accumulate in the center of the wall. The residual stresses were dominated by thermal stresses at low traverse speed, while peening becomes more critical at high traverse speeds. Increasing the powder feed rate increased the magnitude of the residual stresses. High traverse speeds and low feed rates are beneficial for producing 3D parts by CSAM. However, slow traverse speeds are more detrimental than high feed rates for a given layer thickness.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据