期刊
JOURNAL OF NUCLEAR MATERIALS
卷 533, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.jnucmat.2020.152130
关键词
Radiation damage; Proton irradiation; Ion irradiation; TEM
资金
- UK Engineering and Physical Sciences Research Council (EPSRC) [EP/K040375/1]
- Fusion Centre for Doctoral Training (EPSRC) [EP/L01663X/1]
- Platform Grant 'Advanced Nuclear Materials' (EPSRC) [EP/P001645/1]
- US DOE National Scientific Users Facility Program
- U.S. Department of Energy, Office of Nuclear Energy under DOE Idaho Operations Office [DE-AC07-051D14517]
- National Nuclear Users Facility
- Henry Royce Institute (EPSRC) [EP/P021727/1]
- UK National Ion Beam Centre (EPSRC) [NS/A000059/1]
- EPSRC [NS/A000059/1, EP/P001645/1, EP/K040375/1, EP/H018921/1] Funding Source: UKRI
Transmission electron microscopy (TEM) was used to compare the microstructural defects produced in an Fe9Cr model alloy during exposure to neutrons, protons, or self-ions. Samples from the same model alloy were irradiated using fission-neutrons, 2 MeV Fe+ ions or 1.2 MeV protons at similar temperatures (similar to 300 degrees C) and similar doses (similar to 2.0 dpa). The neutron-irradiated alloy contained visible interstitial dislocation loops with b = 111, and on average similar to 5 nm in size. The density varied from 2 +/- 1 x 10(20) m(-3) (in the matrix far from dislocations and boundaries) to 1.2 +/- 0.3 x10(23) m(-3) (close to helical dislocation lines). Chromium alpha'-phase precipitates were also identified at a density of 7.4 +/- 0.4 x10(23) m(-3). Self-ion irradiation produced mostly homogeneously distributed dislocation loops (6-7 nm on average), and with a greater fraction of 100 loops (similar to 40%) than was seen in the neutron-irradiated alloy, and at a density of 6.8 +/- 0.8 x10(22) m(-3). In contrast to the loops produced by neutron irradiation, the self-ion irradiated Fe9Cr contained only vacancy-type loops. Chromium also remained in solution. Proton-irradiated Fe9Cr contained interstitial dislocation loops close to helical-dislocation segments, similar to the neutronirradiated sample. Chromium alpha'-phases were also identified in the proton-irradiated sample at a density of 2.5 +/- 0.3 x 10(23) m(-3), and large voids (up to 7 nm) were found at a density over 10(22)m(-3). Like the neutron-irradiated sample, the density of dislocation loops was also heterogeneously distributed; far from grain boundaries and dislocation lines the density was 2.5 +/- 0.4 x10(22) m(-3), while close to helical dislocation lines the density was 8.1 +/- 1.3 x10(22) m(-3). (c) 2020 Elsevier B.V. All rights reserved.